Diamond ASA C1030H
ASA
利安德巴塞尔(LyondellBasell)
产品描述
Diamond ASA C1030H is a High-Heat Acrylonitrile Styrene Acrylate (ASA) product with excellent Heat-Aging and Weathering properties; Very High Gloss; High Distinctiveness of Image (DOI). ASA C1030H is readily processed by Extrusion and Injection Molding and is available in North America.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热老化高光泽颜色稳定/易着色耐候性 | |||
| 法规认证 | REACH (EC 1907/2006)RoHS(欧盟电子电气设备中有害物质)WEEE(欧盟报废电子气设备) | |||
| 成型方式 | 注塑挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.08 g/cm3 | ASTM D792 | |
熔体质量流动速率(MFR) | |||
220℃/10 kg | 6 g/10 min | ASTM D 1238 | |
230°C/3.8 kg | 1.4 g/10 min | ASTM D 1238 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 48 Mpa | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 38 Mpa | ASTM D638 | 50 mm/min |
拉伸延伸率 | |||
断裂(brk) | 28 % | ASTM D638 | Type I, 50 mm/min |
弯曲强度 | |||
屈服(yld) | 33.8 Mpa | ASTM D790 | 2.0 mm/min |
弯曲模量 | 2500 Mpa | ASTM D790 | 1% Secant, 3.18 mm, 2.0 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 180 J/m | ASTM D256 | |
仪器化落镖冲击能量 | |||
-20℃ (-4℉) 总能量 | 6 J | ASTM D3763 | 6.70 m/sec |
23℃ (73℉)总能量 | 42 J | ASTM D3763 | 6.70 m/sec |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 101 R | ASTM D785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm2） | 98 °C | ASTM D648 | Unannealed, Injection Molded |
1.8 Mpa (264 psi)（18.6kg/cm2） | 84 °C | ASTM D648 | Unannealed |
维卡软化温度(Vicat) | 112 °C | ASTM D1525 | Loading 1 (10 N) |
维卡软化温度(Vicat) | 99 °C | ASTM D1525 | Rate B (120°C/h), Loading 2 (50 N) |