MAGNUM™ 3325 SLG
ABS
盛禧奥(TRINSEO)
产品描述
MAGNUM™ 3325SLG is a medium heat ABS. Its very low gloss combined with a high flow makes it specifically suitable for unpainted interior automotive applications. MAGNUM™ 3325SLG can thereby help you to save up to 50% of the part costs.
Benefits:
Lot to lot consistency allowing for optimal machine parameters settings from the start
Self-coloring enabling improvement of costs by using less pigments and lowering your logistic costs
Low VOC allowing a better interior air quality facing increasing regulatory and OEMs constraints.
Heat stability during wide range of processing temperatures: enhanced part design freedom
High scratch and mar resistance for an improved aesthetic durability of the parts
Easier recyclability of unpainted part
Applications:
Matt/unpainted interior automotive applications
Mid-consoles
Pillars
Door liners
Glove boxes
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热热稳定低光泽耐刮擦低挥发VOC高流动 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.05 g/cm³ | ISO 1183 | |
密度 | 1.05 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
230°C/3.8 kg | 3.1 g/10 min | ASTM D 1238 | |
230°C/3.8 kg | 3.1 g/10 min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.52 % | ISO 294-4 | |
横向(Across Flow) | 0.53 % | ISO 294-4 | |
堆积(视)密度 | 0.69 g/cm³ | ASTM D 1895 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 40 Mpa | ASTM D638 | 51 mm/min |
屈服(yld) | 37 Mpa | ISO 527-2/50 | |
拉伸延伸率 | |||
屈服(yld) | 2.8 % | ASTM D638 | 51 mm/min |
屈服(yld) | 2.8 % | ISO 527-2/50 | |
断裂(brk) | 22 % | ASTM D638 | 51 mm/min |
断裂(brk) | 19 % | ISO 527-2/50 | |
弯曲强度 | |||
- | 64.1 Mpa | ASTM D790 | 1.3 mm/min |
- | 61 Mpa | ISO 178 | 2.0 mm/min |
弯曲模量 | 2140 Mpa | ASTM D790 | 1.3 mm/min |
弯曲模量 | 2070 Mpa | ISO 178 | 2.0 mm/min |
拉伸模量 | 2080 Mpa | ASTM D638 | 51 mm/min |
拉伸模量 | 1920 Mpa | ISO 527-2 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 11 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 16 kJ/m² | ISO 179/1eA | |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 130 J/m | ASTM D256 | |
-30℃ (-22℉) | 11 kJ/m² | ISO 180/A | |
23℃ (73℉) | 190 J/m | ASTM D256 | |
23℃ (73℉) | 18 kJ/m² | ISO 180/A | |
仪器化落镖冲击能量 | |||
-30℃ (-22℉)峰值 | 23 J | ASTM D3763 | |
23℃ (73℉)峰值 | 30 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 96.7 °C | ASTM D648 | Unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 97 °C | ISO 75-2/B | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 82.2 °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 82.2 °C | ISO 75-2/A | Unannealed |
维卡软化温度(Vicat) | 101 °C | ASTM D1525 | Rate A (50°C/h), Loading 2 (50 N) |
维卡软化温度(Vicat) | 101 °C | ISO 306/B50 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 83 E-6 cm/cm/℃ | ASTM E831 | -40 to 100°C |
横向(Across Flow) | 90 E-6 cm/cm/℃ | ASTM E831 | -40 to 100°C |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
FMVSS | 24 mm/min | FMVSS 302 |