MAGNUM™ 357 HP
ABS
盛禧奥(TRINSEO)
产品描述
MAGNUM ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ABS resins are available in a wide range of melt flow rates, impact strength and heat resistance for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion and thermoforming processes.
Automotive MAGNUM ABS resins offer a wide range of gloss, viscosity, impact strength and heat properties for use in numerous automotive applications. Melt flow rates from 1 to 12 g/10 min, impact strengths from 2.5 to 12 ft-lb/in and heat distortion temperatures from 165°F to 190°F are available. Available primarily as natural plus concentrates, MAGNUM ABS resins are used in a wide variety of automotive applications including structural instrument panels, consoles, pillars, and exterior trim parts requiring painting and plating.
MAGNUM™ 357 HP ABS resin is a medium gloss, high heat material that has slightly higher heat resistance and a little higher melt flow rate than MAGNUM 358 HP ABS resin.
基本信息
| 原厂资料 | 物性表-ASTM(英文) | |||
| 产品特性 | 耐热 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.06 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
230°C/3.8 kg | 2 g/10 min | ASTM D 1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.7 % | ASTM D 955 | |
熔体密度 | 1.08 g/cm³ | - | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 37.9 Mpa | ASTM D638 | 51 mm/min |
断裂(brk) | 33.1 Mpa | ASTM D638 | 51 mm/min |
拉伸延伸率 | |||
断裂(brk) | 45 % | ASTM D638 | 51 mm/min |
弯曲强度 | |||
- | 62.1 Mpa | ASTM D790 | 1.3 mm/min |
弯曲模量 | 2210 Mpa | ASTM D790 | 1.3 mm/min |
拉伸模量 | 2000 Mpa | ASTM D638 | 51 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-18℃ (0℉) | 130 J/m | ASTM D 256 | 3.20 mm |
23℃ (73℉) | 310 J/m | ASTM D256 | 3.20 mm |
仪器化落镖冲击能量 | |||
-18℃(0℉)峰值 | 22.6 J | ASTM D 3763 | 3.20 mm,3.39m/sec |
-18℃(0℉)总能量 | 23.7 J | ASTM D 3763 | 3.20 mm,3.39m/sec |
23℃ (73℉)峰值 | 32.8 J | ASTM D3763 | 3.20 mm,3.39m/sec |
23℃ (73℉)总能量 | 42.9 J | ASTM D3763 | 3.20 mm,3.39m/sec |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 104 °C | ASTM D648 | 3.20 mm,Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 87.8 °C | ASTM D648 | 3.20 mm,Unannealed |
维卡软化温度(Vicat) | 120 °C | ASTM D1525 | |
比热容 | 1890 J/kg/℃ | ASTM C 351 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 81 E-6 cm/cm/℃ | ASTM D 696 | |
导热系数 | 0.13 W/(m K) | ASTM C 177 |
原材料现货供应:133-8218-6680(微信同号)