MAGNUM™ 3904
ABS
盛禧奥(TRINSEO)
产品描述
MAGNUM™ 3904 is a medium heat ABS. Its very high impact properties make it suitable for main interior automotive applications. MAGNUM™ 3904 is available in Europe and China, locally produced in major car production regions. Due to its excellent extrusion capabilities, this product is also used for large thermoformed parts, for Truck and Bus applications.
Benefits:
Lot to lot consistency allowing for optimal machine parameters settings from the start
Self-coloring enabling improvement of costs by using less pigments and lowering your logistic costs
Low VOC allowing a better interior air quality facing increasing regulatory and OEMs constraints.
Heat stability during wide range of processing temperatures: enhanced part design freedom
Contains low amounts of gels providing for excellent thermoformability with low levels of scrap
Applications:
Main interior automotive applications requiring high impact
Various interior trims, under the beltline
Large sized applications in commercial transportation
Complies with:
U.S. FDA FCN 1525
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击耐热低挥发VOC | |||
| 法规认证 | FDA(食品药品监督管理局) | |||
| 成型方式 | 注塑挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.05 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
220°C/10.0 kg | 4.7 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
220°C/5.0 kg | 1.2 g/10 min | ASTM D 1238 | |
220℃/10 kg | 4.5 g/10 min | ASTM D 1238 | |
230°C/3.8 kg | 1.2 g/10 min | ASTM D 1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.7 % | ISO 294-4 | |
堆积(视)密度 | 0.65 g/cm³ | ISO 60 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 39 Mpa | ASTM D638 | Injection Molded |
屈服(yld) | 39 Mpa | ISO 527 | 3.20 mm,Injection Molded |
屈服(yld) | 37 Mpa | ISO 527-2/50 | 3.20 mm,Injection Molded |
拉伸延伸率 | |||
屈服(yld) | 3.6 % | ASTM D638 | Injection Molded |
屈服(yld) | 2.8 % | ISO 527 | 3.20 mm,Injection Molded |
屈服(yld) | 2.6 % | ISO 527-2/50 | 3.20 mm,Injection Molded |
弯曲强度 | |||
- | 58 Mpa | ASTM D790 | Injection Molded |
- | 58 Mpa | ISO 178 | 3.20 mm,Injection Molded |
弯曲模量 | 2140 Mpa | ASTM D790 | Injection Molded |
弯曲模量 | 1900 Mpa | ISO 178 | 3.20 mm,Injection Molded |
拉伸模量 | 1880 Mpa | ASTM D638 | |
拉伸模量 | 1820 Mpa | ISO 527-2 | 3.20 mm,Injection Molded |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 18 kJ/m² | ISO 179/1eA | Injection Molded |
-30℃ (-22℉) | 12 kJ/m² | ISO 179/2C | Injection Molded |
23℃ (73℉) | 37 kJ/m² | ISO 179/1eA | Injection Molded |
23℃ (73℉) | 22 kJ/m² | ISO 179/2C | Injection Molded |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 17 kJ/m² | ISO 180/A | Injection Molded |
23℃ (73℉) | 42 kJ/m² | ISO 180/A | Injection Molded |
- | 540 J/m | ASTM D 256 | Injection Molded |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 97 °C | ISO 75-2/A | Annealed |
维卡软化温度(Vicat) | 97 °C | ASTM D1525 | |
维卡软化温度(Vicat) | 97 °C | ISO 306/B50 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | UL94 | |
HB | 3 mm | UL94 | |
燃烧速率 | 40 mm/min | ISO 3795 | 2mm |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
光泽度 | 71 - | ASTM D 523 | |
| 其他性能 | 值/单位 | 测试标准 | 测试条件 |
VOC挥发 | 20 µg/g | VDA 277 |