MAGNUM™ 8391 MED
ABS
盛禧奥(TRINSEO)
产品描述
MAGNUM™ 8391 MED ABS combines an excellent glossy appearance with high flow and medium impact performance. The mass (continuous process) ABS technology ensures an ABS resin that combines excellent processability with a stable light base color that is ideal for self-coloring. MAGNUM 8391 MED natural resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications.
Applications:
Medical Applications
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高光泽医疗级生物相容高流动 | |||
| 法规认证 | ISO10993(生物相容性) | |||
| 颜色形状 | 粒状本色 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.05 g/cm³ | ISO 1183 | |
密度 | 1.05 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
220℃/10 kg | 28 g/10 min | ISO 1133 | |
220℃/10 kg | 28 g/10 min | ASTM D 1238 | |
230°C/3.8 kg | 8 g/10 min | ASTM D 1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.7 % | ASTM D 955 | |
纵向(Flow) | 0.4~0.7 % | ISO 294-4 | |
堆积(视)密度 | 0.65 g/cm³ | ISO 60 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 48 Mpa | ASTM D638 | 50 mm/min |
屈服(yld) | 47 Mpa | ISO 527 | 3.20 mm,Injection Molded |
屈服(yld) | 60 Mpa | ISO 527-2/50 | 3.20 mm,Injection Molded |
断裂(brk) | 35 Mpa | ASTM D638 | 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 2.7 % | ASTM D638 | 50 mm/min |
屈服(yld) | 2.6 % | ISO 527 | 3.20 mm,Injection Molded |
屈服(yld) | 2.5 % | ISO 527-2/50 | 3.20 mm,Injection Molded |
断裂(brk) | 8.7 % | ASTM D638 | 50 mm/min |
弯曲强度 | |||
- | 75 Mpa | ASTM D790 | 1.3 mm/min |
- | 70 Mpa | ISO 178 | 2.0 mm/min |
弯曲模量 | 2480 Mpa | ASTM D790 | 1.3 mm/min |
弯曲模量 | 2400 Mpa | ISO 178 | 2.0 mm/min |
拉伸模量 | 2340 Mpa | ISO 527-2 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 9 kJ/m² | ISO 179/1eA | Injection Molded |
23℃ (73℉) | 19 kJ/m² | ISO 179/1eA | Injection Molded |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 9 kJ/m² | ISO 180/A | Injection Molded |
23℃ (73℉) | 230 J/m | ASTM D256 | |
23℃ (73℉) | 19 kJ/m² | ISO 180/A | Injection Molded |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 108 R | ASTM D785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 87 °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 74 °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 95 °C | ISO 75-2/A | Annealed |
维卡软化温度(Vicat) | 99 °C | ASTM D1525 | Rate B (120°C/h), Loading 1 (10 N) |
维卡软化温度(Vicat) | 95 °C | ISO 306/B50 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | UL94 | |
HB | 3 mm | UL94 | |
燃烧速率 | 60 mm/min | ISO 3795 |