LNP™ LUBRICOMP™ AL003
ABS
沙特基础 (SABIC)
产品描述
LNP* LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing 15% PTFE. Added feature of this material is: Wear Resistant.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐磨 | |||
| 增强填充 | 15% PTFE | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.13 g/cm³ | ISO 1183 | |
密度 | 1.13 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.6~0.8 % | ISO 294 | flow, 24 hrs |
纵向(Flow) | 0.6~0.8 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.8~1 % | ASTM D 955 | xflow, 24 hrs |
横向(Across Flow) | 0.8~1 % | ISO 294 | xflow, 24 hrs |
吸湿率 | 0.31 % | ISO 62 | 23°C / 50% RH |
吸湿率 | 0.2 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 35 Mpa | ASTM D638 | |
屈服(yld) | 35 Mpa | ISO 527 | |
断裂(brk) | 32 Mpa | ISO 527 | |
断裂(brk) | 32 Mpa | ASTM D638 | |
拉伸延伸率 | |||
屈服(yld) | 2.3 % | ASTM D638 | |
屈服(yld) | 2.7 % | ISO 527 | |
断裂(brk) | 14.7 % | ASTM D638 | |
断裂(brk) | 11.6 % | ISO 527 | |
弯曲强度 | |||
- | 62 Mpa | ASTM D790 | |
- | 61 Mpa | ISO 178 | |
弯曲模量 | 2060 Mpa | ASTM D790 | |
弯曲模量 | 2000 Mpa | ISO 178 | |
拉伸模量 | 2410 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2280 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 58 J/m | ASTM D256 | |
23℃ (73℉) | 5 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 202 J/m | ASTM D4812 | |
23℃ (73℉) | 21 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 11 J | ASTM D3763 | |
多轴冲击 | 8 J | ISO 6603 |