LNP™ LUBRICOMP™ AL002
ABS
沙特基础 (SABIC)
产品描述
LNP* LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing 10% PTFE. Added feature of this material is: Wear Resistant.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐磨 | |||
| 增强填充 | 10% PTFE | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.11 g/cm³ | ISO 1183 | |
密度 | 1.1 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | ISO 294 | flow, 24 hrs |
纵向(Flow) | 0.5~0.7 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.5~0.7 % | ASTM D 955 | xflow, 24 hrs |
横向(Across Flow) | 0.5~0.7 % | ISO 294 | xflow, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 37 Mpa | ASTM D638 | |
屈服(yld) | 37 Mpa | ISO 527 | |
断裂(brk) | 32 Mpa | ISO 527 | |
断裂(brk) | 32 Mpa | ASTM D638 | |
拉伸延伸率 | |||
屈服(yld) | 2.6 % | ASTM D638 | |
屈服(yld) | 2.2 % | ISO 527 | |
断裂(brk) | 21 % | ASTM D638 | |
断裂(brk) | 32.2 % | ISO 527 | |
弯曲强度 | |||
- | 62 Mpa | ASTM D790 | |
- | 63 Mpa | ISO 178 | |
弯曲模量 | 2190 Mpa | ASTM D790 | |
弯曲模量 | 2200 Mpa | ISO 178 | |
拉伸模量 | 2130 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 1940 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 58 J/m | ASTM D256 | |
23℃ (73℉) | 5 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 843 J/m | ASTM D4812 | |
23℃ (73℉) | 42 kJ/m² | ISO 180/1U | 80*10*4 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 91 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 92 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 89 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 84 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 95.4 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 96 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 95.4 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 95 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |