CYCOLAC™ INPBMAT
ABS
沙特基础 (SABIC)
产品描述
Cross-linked SAN in styrenic matrix. Provides excellent gloss reduction properties. Maintains original polymer properties such as impact etc. Compatible with various polymer such as PVC and ABS. Can be used in low gloss ABS products at typical loading around 5PHR. Can be effectively compounded with ABS and other styrenic thermoplastics in molded, extruded or calendered applications to provide excellent gloss reduction properties without losing other physical performance.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击低光泽 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.07 g/cm³ | ISO 1183 | |
比重 | 1.07 - | ASTM D792 | |
熔体质量流动速率(MFR) | |||
220℃/10 kg | 0 g/10 min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
弯曲强度 | |||
屈服(yld) | 33 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 38 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 3700 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 3400 Mpa | ISO 178 | 2 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 1 kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | 18 J/m | ASTM D256 | |
23℃ (73℉) | 2 kJ/m² | ISO 180/1A | 80*10*4 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 94 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 86 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 87 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 102 °C | ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 100 °C | ISO 306 | Rate B/50 |