LNP™ LUBRICOMP™ ABL12
ABS
沙特基础 (SABIC)
产品描述
LNP* LUBRICOMP* ABL12 is a compound based on Acrylonitrile Butadiene Styrene resin containing 10% Glass Bead and 5% PTFE. Added feature of this material is: Wear Resistant.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐磨填充增强 | |||
| 增强填充 | 10% 玻璃微珠5% PTFE | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.14 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.1 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.2 % | ASTM D 955 | xflow, 24 hrs |
吸湿率 | 0.2 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 33 Mpa | ASTM D638 | |
屈服(yld) | 32 Mpa | ISO 527 | |
断裂(brk) | 31 Mpa | ISO 527 | |
断裂(brk) | 31 Mpa | ASTM D638 | |
拉伸延伸率 | |||
断裂(brk) | 15 % | ASTM D638 | |
断裂(brk) | 28 % | ISO 527 | |
弯曲强度 | |||
- | 62 Mpa | ASTM D790 | |
- | 59 Mpa | ISO 178 | |
弯曲模量 | 2380 Mpa | ASTM D790 | |
弯曲模量 | 2280 Mpa | ISO 178 | |
拉伸模量 | 2580 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2280 Mpa | ISO 527 | 1 mm/min |
摩擦系数 | 0.39 - | ASTM D 3702 | Dynamic COF |
摩擦系数 | 0.44 - | ASTM D 3702 | Static COF |
磨损因数 | 125 E-10 in5·min/ft·lb·hr | ASTM D 3702 | Wear Factor Washer |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 80 J/m | ASTM D256 | |
23℃ (73℉) | 8 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 560 J/m | ASTM D4812 | |
23℃ (73℉) | 33 kJ/m² | ISO 180/1U | 80*10*4 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 80 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 88 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |