| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.04 g/cm3
| ASTM D 1505 | |
熔体质量流动速率(MFR) | | | |
230℃/10 kg |
7.3 g/10 min | ASTM D 1238 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
47 Mpa | ASTM D638 | 0°C |
屈服(yld) |
43 Mpa | ASTM D638 | 23°C, 43 mm/min |
屈服(yld) |
29 Mpa | ASTM D638 | 71°C |
断裂(brk) |
41 Mpa | ASTM D638 | 0°C |
断裂(brk) |
34 Mpa | ASTM D638 | 23°C |
断裂(brk) |
20 Mpa | ASTM D638 | 71°C |
拉伸延伸率 | | | |
断裂(brk) |
21 % | ASTM D638 | 0°C |
断裂(brk) |
20 % | ASTM D638 | 23°C |
断裂(brk) |
15 % | ASTM D638 | 71°C |
弯曲强度 | | | |
- |
106 Mpa | ASTM D790 | -40°C |
- |
69 Mpa | ASTM D790 | 23°C |
- |
42 Mpa | ASTM D790 | 71°C |
弯曲模量 | 2570 Mpa
| ASTM D790 | 2% Secant, -40°C |
弯曲模量 | 2300 Mpa
| ASTM D790 | 2% Secant, 23°C |
弯曲模量 | 1810 Mpa
| ASTM D790 | 2% Secant, 71°C |
拉伸模量 | 2510 Mpa
| ASTM D638 | 0°C |
拉伸模量 | 2100 Mpa
| ASTM D638 | 23°C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
-40℃ (-40℉) |
150 J/m | ASTM D256 | |
0℃ (32℉) |
320 J/m | ASTM D256 | |
23℃ (73℉) |
520 J/m | ASTM D256 | |
仪器化落镖冲击能量 | | | |
- |
30 J | ASTM D3763 | -30°C |
- |
17 J | ASTM D3763 | -40°C |
- |
42 J | ASTM D3763 | 0°C |
- |
45 J | ASTM D3763 | 23°C |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 101 R
| ASTM D785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm2） |
100 °C | ASTM D648 | Annealed |
0.45 Mpa (66 psi)（4.6kg/cm2） |
91 °C | ASTM D648 | Unannealed, 3.18 mm |
1.8 Mpa (264 psi)（18.6kg/cm2） |
95 °C | ASTM D648 | Annealed, 3.18 mm |
1.8 Mpa (264 psi)（18.6kg/cm2） |
76 °C | ASTM D648 | Unannealed, 3.18 mm |
维卡软化温度(Vicat) | 105 °C
| ASTM D1525 | Rate A (50°C/h), Loading 1 (10 N) |
维卡软化温度(Vicat) | 95 °C
| ASTM D1525 | Rate A (50°C/h), Loading 2 (50 N) |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
HB |
1.5 mm | UL94 | |