| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.02 g/cm3
| ASTM D792 | |
熔体质量流动速率(MFR) | | | |
220℃/10 kg |
7.3 g/10 min | ASTM D 1238 | |
230°C/3.8 kg |
1.2 g/10 min | ASTM D 1238 | |
收缩率 | | | |
纵向(Flow) |
0.7 % | ASTM D 955 | 48 hr |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
41.5 Mpa | ASTM D638 | 23°C, 3.18 mm, Injection Molded, 50 mm/min |
断裂(brk) |
31.8 Mpa | ASTM D638 | 23°C, 3.18 mm, Injection Molded, 50 mm/min |
拉伸延伸率 | | | |
断裂(brk) |
17 % | ASTM D638 | 23°C, Injection Molded, 50 mm/min |
弯曲强度 | | | |
- |
60.5 Mpa | ASTM D790 | 23°C, 3.18 mm, Injection Molded, 1.3 mm/min |
弯曲模量 | 1900 Mpa
| ASTM D790 | 23°C, 3.18 mm, Injection Molded, 1.3 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
-20℃ (-4℉) |
290 J/m | ASTM D256 | 3.18 mm |
0℃ (32℉) |
330 J/m | ASTM D256 | 3.18 mm |
23℃ (73℉) |
430 J/m | ASTM D256 | 3.18 mm, Injection Molded |
仪器化落镖冲击能量 | | | |
- |
4.16 J | ASTM D3763 | 0°C, 2.04 m/sec |
- |
4.11 J | ASTM D3763 | 23°C, 2.04 m/sec |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm2） |
89 °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm2） |
76 °C | ASTM D648 | Unannealed |
维卡软化温度(Vicat) | 103 °C
| ASTM D1525 | Rate A (50°C/h), Loading 1 (10 N) |
维卡软化温度(Vicat) | 92 °C
| ASTM D1525 | Rate A (50°C/h), Loading 2 (50 N) |
维卡软化温度(Vicat) | 106 °C
| ASTM D1525 | Rate B (120°C/h), Loading 1 (10 N) |
维卡软化温度(Vicat) | 95 °C
| ASTM D1525 | Rate B (120°C/h), Loading 2 (50 N) |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
光泽度 | 90 -
| ASTM D 523 | 60° |