POLIMAXX SP100W(A)
ABS
泰国石化(IRPC)
产品描述
SP100(W) is an ABS grade with a UV additive that provides very high impact strength and weathering performance. It is designed for injection molding processing requiring high impact loading while also preventing yellowness such as appliance & electronic parts and automotive parts.
INDUSTRY
-Appliance & Electronic Parts
-Interior Parts
PRODUCT FEATURE
-Super High Impact Strength
-Good Stiffness
-Glossy Finish Parts
-Weathering Performance
REGULATION COMPLIANCE
-RoHS Directive 2011/65/EU
-REACH Regulation (EC) No. 1907/2006
-UL Yellow Card: E132283
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 良好的刚性高冲击高光泽抗紫外线耐候性 | |||
| 添加助剂 | 紫外线稳定剂 | |||
| 法规认证 | REACH (EC 1907/2006)RoHS(欧盟电子电气设备中有害物质)UL QMFZ2(UL认证) | |||
| 成型方式 | 注塑 | |||
| 应用产品 | 电子电器汽车零部件汽车内饰件 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.05 g/cm3 | ASTM D792 | 23°C |
熔体质量流动速率(MFR) | |||
220℃/10 kg | 18 g/10 min | ASTM D 1238 | |
收缩率 | |||
- | 0.4~0.6 % | Internal | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 450 kg/cm2 | ASTM D638 | 3.2 mm, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 20 % | ASTM D638 | 3.2 mm, 5 mm/min |
弯曲强度 | |||
- | 610 kg/cm2 | ASTM D790 | 6.4 mm, 2.5 mm/min |
弯曲模量 | 22000 kg/cm2 | ASTM D790 | 1% Secant, 6.4 mm |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 35 kg·cm/cm | ASTM D256 | 6.4 mm |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 108 R | ASTM D785 | 6.4 mm |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm2） | 85 °C | ASTM D648 | 6.4 mm, Unannealed |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | UL94 |