中国GBT ZG30Cr20Ni10(ZG3Cr20Ni10)大型耐热钢铸件和ZG30Cr20Ni10(ZG3Cr20Ni10)机械性能、化学成分、对照参考、数据表.
数据表：钢种：特殊合金：ZG30Cr20Ni10(ZG3Cr20Ni10)
ZG30Cr20Ni10(ZG3Cr20Ni10)属性
| 类别 | 类型 | 钢种 | 标准 | 国家 | 应用 |
|---|
| 钢种 | 特殊合金 | ZG30Cr20Ni10(ZG3Cr20Ni10) | GBT | 中国 | 大型耐热钢铸件 |
| - | - | ZG08Cr19Ni9(ZG0Cr19Ni9) |
- | - | - |
| - | - | ZG08Cr19Ni11Mo3(ZG0Cr19Ni11Mo3) |
- | - | - |
| - | - | ZG12Cr22Ni12(ZG1Cr22Ni12) |
- | - | - |
| - | - | ZG20Cr25Ni20(ZG2Cr25Ni20) |
- | - | - |
| - | - | ZG12Cr17Mn9Ni4Mo3Cu2N(ZG1Cr17Mn9Ni4Mo3Cu2N) |
- | - | - |
| - | - | ZG12Cr18Mn13NiMo2CuN(ZG1Cr18Mn13Mo2CuN) |
- | - | - |
| - | - | ZG40Cr9Si2(ZG4Cr9Si2) | - | - | - |
| - | - | ZG30Cr18Mn12Si2N(ZG3Cr18Mn12Si2N) |
- | - | - |
| - | - | ZG35Cr24Ni7SiN |
- | - | - |
| - | ZG20Cr26Ni5(ZG3Cr25Ni5) |
- | - | - |
ZG30Cr20Ni10(ZG3Cr20Ni10)的化学成分(质量分数)(wt.%)
| C(％) | Si(％) | Mn(％) | P(％) | S(％ ) | Cr(％) | Ni(％) | Mo(％) |
|---|
| 0.20-0.40 | ≤2.00 | ≤2.00 | 0.04 | 0.04 | 18.0-23.0 | 8.0-12.00 | ≤0.50 |
钢种机械性能ZG30Cr20Ni10(ZG3Cr20Ni10)
| 屈服强度 Rp0.2 (MPa) |
拉伸强度 Rm (MPa) |
冲击性能 KV/Ku (J) |
伸长率 A (%) | 断裂横截面减少 Z (%) |
热处理状态 | 布氏硬度 (HBW) |
|---|
| 348（≥） | 374（≥） | 11 | 21 | 42 | 固溶和老化、退火、Ausaging、Q+T等 | 231 |
钢种物理性能ZG30Cr20Ni10(ZG3Cr20Ni10)
| 温度 (°C) |
弹性模量 (GPa) |
20(°C) 至 之间的平均热膨胀系数 10-6/(°C) | 导热系数 (W/m·°C) |
比热容 (J/kg·°C) |
电阻率 (Ω mm2/m) |
书房体积 (kg/dm3) |
泊松系数，ν |
|---|---|---|---|---|---|---|---|
| 42 | - | - | - | - | 0.23 | - | - |
| 281 | 699 | - | 21.3 | 212 | - | - | - |
| 567 | - | 23 | 23.2 | - | - | 422 | 331 |
钢种的热处理ZG30Cr20Ni10(ZG3Cr20Ni10)
热处理：1475°C - 1621°C
技术曲线钢种工艺曲线ZG30Cr20Ni10(ZG3Cr20Ni10)
无曲线
ZG30Cr20Ni10(ZG3Cr20Ni10) 对照表（等效牌号）
| 钢材等级 | 标准 | 国家 | 应用 |
|---|
| ZG30Cr20Ni10(ZG3Cr20Ni10) | GBT | 中国 | 大型耐热钢铸件 |