中国 GBT ZG12Cr18Mn13NiMo2CuN(ZG1Cr18Mn13Mo2CuN) 重型不锈钢铸件和 ZG12Cr18Mn13NiMo2CuN(ZG1Cr18Mn13Mo2CuN) 机械性能、化学成分、对照参考、数据表.
数据表：钢种：特殊合金：ZG12Cr18Mn13NiMo2CuN(ZG1Cr18Mn13Mo2CuN)
ZG12Cr18Mn13NiMo2CuN(ZG1Cr18Mn13Mo2CuN)属性
| 类别 | 类型 | 钢种 | 标准 | 国家 | A应用 |
|---|
| 钢种 | 特殊合金 | ZG12Cr18Mn13NiMo2CuN(ZG1Cr18Mn13Mo2CuN) | GBT | 中国 | 重型不锈钢铸件 |
| - | - | ZG20Cr13(ZG2Cr13) |
- | - | - |
| - | - | ZG30Cr13(ZG3Cr13) |
- | - | - |
| - | - | ZG12Cr18Ni9Ti(ZG12Cr18Ni9Ti) |
- | - | - |
| - | - | ZG06Cr13Ni4Mo(ZG0Cr13Ni4Mo) |
- | - | - |
| - | - | ZG06Cr13Ni6Mo(ZG0Cr13Ni6Mo) |
- | - | - |
| - | - | ZG08Cr19Ni9(ZG0Cr19Ni9) |
- | - | - |
| - | - | ZG08Cr19Ni11Mo3(ZG0Cr19Ni11Mo3) |
- | - | - |
| - | - | ZG12Cr22Ni12(ZG1Cr22Ni12) |
- | - | - |
| - | - | ZG20Cr25Ni20(ZG2Cr25Ni20) |
- | - | - |
| - | - | ZG12Cr17Mn9Ni4Mo3Cu2N(ZG1Cr17Mn9Ni4Mo3Cu2N) |
- | - | - |
ZG12Cr18Mn13NiMo2CuN(ZG1Cr18Mn13Mo2CuN)的化学成分(质量分数)(wt.%)
| C(％) | Si(％) | Mn(％) | P(％) | S(％ ) | Cr(％) | Ni(％) | Mo(％) |
|---|
| ≤0.12 | ≤1.50 | 12.0-14.0 | 0.06 | 0.035 | 17.0-20.0 | － | 1.50-2.00 |
钢种机械性能ZG12Cr18Mn13NiMo2CuN(ZG1Cr18Mn13Mo2CuN)
| 屈服强度 Rp0.2 (MPa) |
拉伸强度 Rm (MPa) |
冲击性能 KV/Ku (J) |
伸长率 A (%) |
断裂横截面减少 Z (%) |
热处理状态 | 布氏硬度 (HBW) |
|---|
| 498（≥） | 841（≥） | 31 | 12 | 31 | 固溶和老化、退火、Ausaging、Q+T等 | 341 |
钢种物理性能ZG12Cr18Mn13NiMo2CuN(ZG1Cr18Mn13Mo2CuN)
| 温度 (°C) |
弹性模量 (GPa) |
20(°C) 至 之间的平均热膨胀系数 10-6/(°C) | 导热系数 (W/m·°C) |
比热容 (J/kg·°C) | 电阻率 (Ω mm2/m) |
密度 (kg/dm3) |
泊松系数，ν |
|---|---|---|---|---|---|---|---|
| 34 | - | - | - | - | 0.42 | - | - |
| 288 | 635 | - | 34.3 | 112 | - | - | - |
| 413 | - | 21 | 33.2 | - | - | 214 | 322 |
钢种的热处理ZG12Cr18Mn13NiMo2CuN(ZG1Cr18Mn13Mo2CuN)
热处理：1471°C - 1126°C
技术曲线钢种工艺曲线ZG12Cr18Mn13NiMo2CuN(ZG1Cr18Mn13Mo2CuN)
无曲线
对照引用表（等效 Grade) ZG12Cr18Mn13NiMo2CuN(ZG1Cr18Mn13Mo2CuN)
| 钢材等级 | 标准 | 国家 | 应用 |
|---|
| ZG12Cr18Mn13NiMo2CuN(ZG1Cr18Mn13Mo2CuN) | GBT | 中国 | 重型不锈钢铸件 |